Compressed Air Distribution- FR Composite Pneumatic Pipe

Technical Details (MOC)


Upper & Inner Layer – Poly Propylene Impact Copolymer

Middle Layer – Glass Fibre Reinforcement 

Technical Parameters

  • R.A. Value – 0.01 Micron
  • Vicat Softening Point – 145 Deg C
  • Melting Temperature Rang – 150-160 Deg.
  • Tensile Strength at Break – 45 MPa
  • Flexural Modulus – 1350 MPa
  • Coefficient of Linear Expansion – 1.0X10-4

Temperature Resistance

0 Deg. To 100 Deg Temperature resistance

0 Deg to 95 Deg Working Temperature Resistance

U.V. Resistance

Specialized U.V. Treated pipe With Carbon Compounded U.V. Layer on Upper side For Outdoor Application Areas.

Pressure withstand Capacity & Size Availability

4 options available :

  1. SDR5 – PN25 :- 20mm to 160 mm OD
  2. SDR6 – PN20 :- 20mm to 160 mm OD
  3. SDR7.4 – PN16 :- 20mm to 160 mm OD
  4. SDR11 – PN10 :- 50 mm to 160 mm OD

Industrial Standards Met

Pipe: DIN8077-78

Fittings: DIN16962 – Part 5 to Part 10


Jointing System

Socket Fusion Welding

Special Features of Product

  • Lowest Thermal Expansion, Least expansion in comparison to other products, so requires Less clamping compared to any other polymer Piping & similar requirement as Metal piping
  • Least RA Value 0.1 Micron, Ensuring Least Frictional Loss
  • Latest Socket Fusion Welding Technology. Giving 100% Leak Proof Joints till Life of Pipe.

Applications  Areas:-

  1. Compressed Air
  2. Instrumentation Air
  3. Hot Air
  4. Nitrogen
  5. 5.    Vacuum Line

Replacement/Substitute For

GI, MS, ERW, SS, Aluminum, CS, Composite, PPR Plumbing Pipes,

Salient Features of Anjney

  • Very Low Thermal Expansion due to Sandwich Fibreglass Reinforcement.
  • As a result of Socket Fusion joints there is 0 % leakage
  • 100% Non Corrosive Non Erosive Material Giving Leak proof life without Maintenance
  • Superior Quality of Air due to no rust formation on pipe
  • 0.1 Micron RA value and mirror finish inner surface, ensures 40 % to 60 % lesser friction loss compared to other pipes
  • High temperature and high Pneumetic pressure withstand capacity due to Inbuilt FR Reinforcement Layer



FR Composite Pneumatic Pipe Catalog